What is shotcrete, its properties, uses and advantages?

Shotcreting is a process that involves spraying or depositing mortar made from very fine concrete on a prepared surface. The spray velocity is very high, and the material deposited on the surface is called shotcrete. It has different names depending on the country, like Nucrete, Torkrete, Guncrete, Blastcrete, etc.

Shotcrete has many advantages over traditional concrete, and it requires a smaller portable plant to manufacture and place.

It can bond well with many materials, so this is something to consider.

Shotcrete, like all concretes, requires proper curing to prevent cracks. Shotcrete should also be curled with water for at least 14 days after setting the concrete. Spray concrete that has been properly cured can reach strengths of 450-550 kg/cm2 within 28 days.

What is Shotcrete?

Shotcrete is concrete that has been pumped through a hose to be pneumatically projected at high velocity onto the surface. It is a construction technique. It is a spray concrete mixed with water and sprayed in a predetermined amount of cement and aggregates. Dr Akeley was the first to use shotcrete in Pennsylvania, USA, in 1907.

Shotcrete can cause compaction and placement due to the force projected using a nozzle. It can impact any surface or shape, even vertical or overhead. This technology allows for completing construction tasks with great economies in both time and money. This technology saves time and money.

Shotcrete was developed to speed up the work and reduce any architectural effects or modifications. Technical properties like compressive strength and elastic modulus of young shotcrete significantly impact safety in tunnels, the lining of canals, and building construction, during the construction period.

Shotcrete can be used to stabilise and support structures in a short time. It also allows concrete applications without the use of moulds. Shotcrete, also known as 'SprayedConcrete', results from the interaction between concrete and machine. The need for underground infrastructure is growing in times of increasing mobility and restricted space. In that case, shotcrete has an important role in fulfilling the requirements.

What are the two basic shotcreting processes?

There are two basic shotcreting processes:

1. Dry Mix Process

It involves the cement mixture being transported through a delivery pipe to a special delivery equipment machine.

A distributor or feed wheel feeds the mixture into the delivery tube. This material is carried by compressed air perforated manifold. Water is introduced under pressure and mixed in with other ingredients.

The mortar was hurled from the nozzle at high speed onto the surface to be shotcrete. The nozzleman can alter the water quantity easily during this process.

Concrete with a higher water content will tend to slump when poured on top of a vertical surface. You should adjust the amount of water to minimise material wastage. The water-cement ratio should range from 0.33 to 0.50.

Shotcrete can be made with a variety of equipment. Equipment that ensures a constant mortar supply can transport the material up to 300-500 m horizontally and 45-100 m vertically.

2. Wet Mix Process

All the ingredients, such as cement, sand, and small-sized coarse aggregate, are combined before entering the delivery equipment chamber.

The ready-mixed concrete is metered in 7 atmospheres to the nozzle. Additional air is injected at the nozzle to increase velocity and improve the running pattern. There is equipment that can place concrete at 3 to 9m3/hour.

Rebound refers to concrete or mortar falling back onto the surface being treated due to high velocity. It depends on the water-cement ratio and the location and nature of the treated surface.

The range of rebounds for horizontal slabs is between 5 and 15% for vertical surfaces and sloping, 15 to 30% for vertical surfaces and sloping, and 20 to 50 per cent for overhead surfaces and corners.

For lightweight concrete, the dry mix process is preferred. A lower water-cement ratio results in stronger concrete, less shrinkage and creep, and greater durability. Using air-entraining agents in the dry process can help achieve greater durability.

The water-cement ratio is very accurately controlled in the wet processes. The wet process does not cause the most problems. Concrete placement rates are higher when there is more concrete to be placed.

Shotcrete Properties

Some of the shotcrete properties are:

1. Cement content is high, and aggregates are limited in size.

2. In most cases, it should increase durability.

3. Conventional concrete is consolidated through vibration. Shotcrete is consolidated when a high-velocity jet impacts the surface. It increases cement content by a rebound and creates different air-void systems that affect shotcrete's durability.

4. The application process affects shotcrete's in-place properties more than the mixture proportions.

5. Shotcrete specimens are usually made from test panels measuring approximately one-meter square and 75mm thick. They are typically sawed using plywood gunned from.

Shotcrete Applications

The applications of shotcrete are:

1. Shotcrete is widely used in various constructions, including thin overhead vertical or horizontal surfaces, especially the curved or folded sections and canal, reservoir, or tunnel lining.

2. It is also used in water retention structures and prestressed tank applications.

3. Shotcrete has been successfully used to stabilise rock slopes and temporarily protect newly excavated rock surfaces.

4. It protects against long-term corrosion of oil tanks, pilling, co bunker, and steel building frames.

5. These are used in high-temperature applications such as the refractory liner of kilns and chimneys, furnaces, and similar areas.

Advantages of Shotcrete

The advantages of shotcrete are:

1. Spray concrete, also known as sprayed concrete, is a form of concrete used to encapsulate and protect the area. Shotcreting is easy to apply in restricted areas far from the access point. Concrete mix is transported a great distance from the production site using this method.

2. Shotcrete is a structurally strong, durable material that can bond well with concrete, steel, and masonry. Shotcrete has a water-cement ratio of 0.35 to 0.5 per mass, which is lower than other concrete. The compressive strength reported is between 20 and 50 N/mm2.

3. Shotcrete generally has a 0.6 to 0.1% drying shrinkage value. Shotcrete is very durable in both laboratory and field environments.

4. Most importantly, shotcrete is superior to other concrete in many ways.